| 초록 |
In this study, to increase the strength and enhance the sintering property of $Al_2O_3$ , $Y_2O_3$ and $La_2O_3$ were added; the effects of these additions on the sintering characteristics of $Al_2O_3$ were observed. Adding 1% of $Y_2O_3$ to $Al_2O_3$ repressed the development of abnormal particles and reduced the grain boundary migration of $Al_2O_3$ , curbing pores to capture particles; as such, the material showed a fine microstructure. But, when over 2% of $Y_2O_3$ was added, the sintering property was reduced because of abnormal particle grain growth and pore formation in particles. Adding 1% of $Y_2O_3$ and $La_2O_3$ to $Al_2O_3$ led to the development of abnormal particles and formed pores in the particles; when over 3% of $La_2O_3$ was added, the sintering property was reduced because the shape of the $Al_2O_3$ particles changed to angled plates. |