Pd 나노 촉매가 도입된 나피온 막의 기계적 강도 및 고분자 전해질막 연료전지 (PEMFC) 성능
논문 개요
| 기관명 | NDSL |
|---|---|
| 저널명 | 한국수소 및 신에너지학회 논문집 = Transactions of the Korean Hydrogen and New Energy Society |
| ISSN | 1738-7264, |
| ISBN |
논문저자 및 소속기관 정보
| 저자(한글) | 이우금,이홍기 |
|---|---|
| 저자(영문) | |
| 소속기관 | |
| 소속기관(영문) | |
| 출판인 | |
| 간행물 번호 | |
| 발행연도 | 2016-01-01 |
| 초록 | A simple solid state incorporation method was employed in order to incorporate Pd nanocatalyst into a Nafion film for polymer electrolyte membrane fuel cell (PEMFC) via the reduction of palladium (II) bis (acetylacetonate), $Pd(acac)_2$ . It was sublimed, penetrated into Nafion film and then reduced to Pd nanoparticles simultaneously in a glass reactor of N2 atmosphere at $180^{ circ}C$ for 1, 3 and 5 min. This reaction was took place without any reducing agent and any solvent. The morphology of the Pd nanoparticles was observed by transmission electron microscopy (TEM), and Pd distribution was analyzed by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). And 23% modification of tensile strength of Pd/Nafion composite film was measured by universal testing machine and I-V curve was estimated by using a unit cell with $5{ times}5cm^2$ active area. |
| 원문URL | http://click.ndsl.kr/servlet/OpenAPIDetailView?keyValue=03553784&target=NART&cn=JAKO201621650494247 |
| 첨부파일 |
추가정보
| 과학기술표준분류 | |
|---|---|
| ICT 기술분류 | |
| DDC 분류 | |
| 주제어 (키워드) | 고분자 전해질막,연료전지,팔라듐 촉매,백금 촉매,고상 합침법,Polymer electrolyte membrane,Fuel cell,Pd catalyst,Pt catalyst,Solid state incorporation method |