| 초록 |
The effects of surface modification by nitric acid on the pre-treatment of electroless copper plating were investigated. Copper was electroless-plated on the nitric acid treated graphite activated by a two-step pre-treatment process (sensitization + activation). The chemical state and relative quantities of the various surface species were determined by X-ray photoelectron spectroscopy (XPS) after nitric acid modification or pre-treatment. The acid treatment increased the surface roughness of the graphite due to deep and fine pores and introduced the oxygen-containing functional groups (-COOH and O-C=O) on the surface of graphite. In the pre-treatment step, the high roughness and many functional groups on the nitric acid treated graphite promoted the adsorption of Sn and Pd ions, leading to the uniform adsorption of catalyst ( $Pd^0$ ) for Cu deposition. In the early stage of electroless plating, a lot of tiny copper particles were formed on the whole surface of acid treated graphite and then homogeneous copper film with low variation in thickness was formed after 30 min. |